NOTES/APPLICATION
Turquoise, transparent, glossy crackle glaze, must be applied in one coat only since it tends to run strongly
To prevent formation blisters, biscuit fire at 1000 °C
Can show blisters on some sorts of clay when applied on both sides/all around
Crackles develop mostly after cooling in the kiln and this is reinforced in time, partially up to 1 week
If crackles did not develop, the glaze can also be removed from the kiln at approx. 100 °C and quenched with cold water
The crackle net is inked, e.g. with black China ink, multi-coloured acrylic paints, strong black tea or else
With a slightly thicker coat on horizontal surfaces such as the inner surface of plates and bowls, interesting, darker turquoise scale crackles stars to form on some clays.
PROPERTIES
glossy
tends to run strongly
consistent in firing range 1020°-1060°
forms cracks
Raku suitable
semi-transparent
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
delicate light pink with natural brown speckles
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: delicately speckled with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive pastel shades, speckles become streaks on vertical surfaces / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
Raku suitable
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
warm and striking turqouise with natural brown speckles
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: delicately speckled with a rather semi-transparent surface / apply 2 layers
at 1250°C: glassy, semi-transparent surface with intensive pastel shades, speckles become streaks on vertical surfaces / apply 2 layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
Raku suitable
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
very gentle white colour with natural brown speckles
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: delicately speckled with a rather semi-transparent surface / apply 2 layer
at 1250°C: glassy, semi-transparent surface with intensive pastel shades, speckles become streaks on vertical surfaces / apply 2 layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
Raku suitable
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
strong shining blueish gray
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: bright colourfulness with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive Pastel shades, awesome also on porcelain mass / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
Raku suitable
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
strong shining dark green, very close to classical bottle green
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: bright colourfulness with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive Pastel shades, awesome also on porcelain mass / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
Raku suitable
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
strong shining and pastel colours
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: bright colourfulness with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive Pastel shades, awesome also on porcelain mass / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
Raku suitable
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
strong shining and pastel colours
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: bright colourfulness with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive Pastel shades, awesome also on porcelain mass / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
strong shining and pastel colours
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: bright colourfulness with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive Pastel shades, awesome also on porcelain mass / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
semi-transparent
recommended for tableware
NOTES/APPLICATION
striking, semi-transparent glaze with a great glassy surface
strong shining and pastel colours
very easy to use in a broad firing range from 1020° to 1280°C (cone 05-04 to cone 8-9)
at 1050°C: very colourful and almost opaque / apply 2-3 times
at 1150°C: bright colourfulness with a rather semi-transparent surface / apply two layers
at 1250°C: glassy, semi-transparent surface with intensive Pastel shades, awesome also on porcelain mass / apply two layers
tends to run when applied thickly from 1150°C on
perfect for tableware
works greatly also in combination with BOTZ Unidekor
PROPERTIES
glossy
tends to run
consistent in firing range 1020°-1280°C
semi-transparent
recommended for tableware